ALLOY 6063 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Al |
MIN | 0.45 | 0.18 | - | - | 0.45 | - | - | - | B1 |
MAX | 0.50 | 0.22 | 0.02 | 0.03 | 0.60 | 0.02 | 0.04 | 0.04 | |
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T4 | 95 | 190 | 20 | 47 | |||||
T5 | 220 | 250 | 16 | 81 | |||||
Special Properties | |||||||||
Formed - Good | Mechanized – Moderate | Soldering - All | |||||||
Corrosion - Good | Finishes – Very Good | Anodized – Very Good | |||||||
Typical Applications | |||||||||
Architecture in general, window construction, glazing and facades, renewable energies, transport industry. |
ALLOY 6005 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Al |
MIN | 0.58 | 0.18 | 0.18 | 0.03 | 0.52 | - | 0.01 | 0.05 | B1 |
MAX | 0.65 | 0.25 | 0.25 | 0.08 | 0.60 | 0.08 | 0.04 | 0.01 | |
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T4 | 105 | 215 | 21 | 71 | |||||
T6 | 290 | 315 | 13 | 107 | |||||
Special Properties | |||||||||
Formed - Good | Mechanized – Moderate | Soldering – MG, TIG | |||||||
Corrosion - Good | Finishes – Very Good | Anodized – Protection | |||||||
Typical Applications | |||||||||
Construction, automobile industry, transport industry, renewable energies, general transport, heavy structures. |
ALLOY 6060 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Al |
MIN | 0.35 | - | - | - | 0.35 | - | - | - | B1 |
MAX | 0.50 | 0.25 | 0.10 | 0.10 | 0.55 | 0.05 | 0.05 | 0.10 | |
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T5 | 105 | 85 | 10 | 55 | |||||
T6 | 290 | 220 | 18 | 107 | |||||
Special Properties | |||||||||
Formed - Good | Mechanized – Moderate | Soldering - TIG | |||||||
Corrosion - Good | Finishes – Very Good | Anodized – Good | |||||||
Typical Applications | |||||||||
Architectural structures, doors, windows, walls, stairs, fences, heat sinks, structures which require good superficial finishes. |
ALLOY 6061 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Al |
MIN | 0.40 | 0.18 | - | - | 0.80 | - | - | 0.04 | B1 |
MAX | 0.80 | 0.25 | 0.15 | 0.5 | 1.20 | 0.25 | 0.15 | 0.35 | |
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T4 | 105 | 215 | 21 | 71 | |||||
T6 | 290 | 315 | 13 | 107 | |||||
Special Properties | |||||||||
Formed - Good | Mechanized – Moderate | Soldering – MG, TIG | |||||||
Corrosion - Good | Finishes – Very Good | Anodized – Protection | |||||||
Typical Applications | |||||||||
Construction, automobile industry, transport industry, renewable energies, general transport, heavy structures. |
ALLOY 6082 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Others |
MIN | 0.7 | 0.5 | 0.10 | 0.40 | 0.60 | 0.20 | 0.10 | 0.25 | 0.15 |
MAX | 1.3 | 1.00 | 1.20 | ||||||
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T4 | 120 | 230 | 16 | 58 | |||||
T6 | 270 | 330 | 10 | 93 |
ALLOY 6351 | |||||||||
---|---|---|---|---|---|---|---|---|---|
% | Si | Fe | Cu | Mn | Mg | Zn | Ti | Cr | Others |
MIN | 0.7 | 0.5 | 0.1 | 0.4 | 0.4 | 0.2 | 0.2 | - | 0.15 |
MAX | 1.3 | 0.8 | 0.8 | ||||||
Mechanical Characteristics | |||||||||
Temper (AA) | LIMIT (Mpa) | BREAKING POINT (Mpa) | LENGTHENING (%) | HARDNESS (Brinel) | |||||
T4 | 140 | 240 | 18 | 65 | |||||
T6 | 270 | 310 | 11 | 95 |